Method of making grid lines for thermally-transferred color filter array element

ABSTRACT

A process of making opaque grid lines for a color filter array element comprising 
     a) exposing a photographic element comprising an unhardened gelatin-silver halide emulsion coated on a support to light through a mask which defines the grid pattern, the emulsion being coated at a total dry weight coverage of at least 0.5 g/m 2  ; 
     b) developing the element with a tanning developer to develop the exposed areas of grid lines; 
     c) washing off the undeveloped emulsion leaving the grid line pattern on the element; and 
     d) drying the element to produce open cells on the support divided by opaque lines of silver in hardened gelatin greater than 0.3 μm in height above the support. 
     In a preferred embodiment, the process includes the further steps of: 
     d) coating the cellular element with a polymeric dye-receiving layer; and 
     e) thermally transferring individual dyes to form a color filter array element comprising a repeating mosaic pattern of colorants in a polymeric binder, the pattern being made up of color patches bounded by the opaque lines in a grid pattern.

This invention relates to a method of making grid lines for a thermally-transferred color filter array element which is used in various applications such as a liquid crystal display device.

In recent years, thermal transfer systems have been developed to obtain prints from pictures which have been generated electronically from a color video camera. According to one way of obtaining such prints, an electronic picture is first subjected to color separation by color filters. The respective color-separated images are then converted into electrical signals. These signals are then operated on to produce cyan, magenta and yellow electrical signals. These signals are then transmitted to a thermal printer. To obtain the print, a cyan, magenta or yellow dye-donor element is placed face-to-face with a dye-receiving element. The two are then inserted between a thermal printing head and a platen roller. A line-type thermal printing head is used to apply heat from the back of the dye-donor sheet. The thermal printing head has many heating elements and is heated up sequentially in response to the cyan, magenta and yellow signals. The process is then repeated for the other two colors. A color hard copy is thus obtained which corresponds to the original picture viewed on a screen. Further details of this process and an apparatus for carrying it out are contained in U.S. Pat. No. 4,621,271 by Brownstein entitled "Apparatus and Method For Controlling A Thermal Printer Apparatus," issued Nov. 4, 1986, the disclosure of which is hereby incorporated by reference.

Liquid crystal display devices are known for digital display in electronic calculators, clocks, household appliances, audio equipment, etc. There has been a need to incorporate a color display capability into such monochrome display devices, particularly in such applications as peripheral terminals using various kinds of equipment involving phototube display, mounted electronic display, or TV-image display. Various attempts have been made to incorporate a color display using a color filter array element into these devices. However, none of the color array elements for liquid crystal display devices so far proposed have been successful in meeting all the users needs.

One commercially-available type of color filter array element which has been used in liquid crystal display devices for color display capability is a transparent support having a gelatin layer thereon which contains dyes having the additive primary colors red, green and blue in a mosaic pattern obtained by using a photolithographic technique. To prepare such a color filter array element, a gelatin layer is sensitized, exposed to a mask for one of the colors of the mosaic pattern, developed to harden the gelatin in the exposed areas, and washed to remove the unexposed (uncrosslinked) gelatin, thus producing a pattern of gelatin which is then dyed with dye of the desired color. The element is then recoated and the above steps are repeated to obtain the other two colors. This method contains many labor-intensive steps, requires careful alignment, is time-consuming and very costly. Further details of this process are disclosed in U.S. Pat. No. 4,081,277.

In addition, a color filter array element to be used in a liquid crystal display device may have to undergo rather severe heating and treatment steps during manufacture. For example, a transparent electrode layer, such as indium tin oxide, is usually vacuum sputtered onto the color filter array element. This may take place at temperatures elevated as high as 200° C. for times which may be one hour or more. This is followed by coating with a thin alignment layer for the liquid crystals, such as a polyimide. Regardless of the alignment layer used, the surface finish of this layer in contact with the liquid crystals is very important and may require rubbing or may require curing for several hours at an elevated temperature. These treatment steps can be very harmful to many color filter array elements, especially those with a gelatin matrix.

Opaque grid lines are normally used in these color filter array elements to separate the mosaic elements or color patches from each other and to prevent color contamination or light flare.

Grid lines are made in a prior art method by evaporating onto the substrate chromium oxide through a photolithographic mask which defines the grid pattern. There is a problem with using grid lines obtained in that manner with a thermally-obtained color filter array element in that the height of such grid lines, e.g., less than 1 μm, is too small relative to the thickness of the individual elements of the color filter array. In a thermally-transferred color filter array element, the mosaic elements or color patches are about 2 μm thick, so that the grid lines will not prevent dye from wandering from one mosaic element or color patch to another. In addition, color filter array elements to be used in liquid crystal display devices are subjected to the severe heating and treatment steps described above which would further aggravate the dye-mixing problem.

It would be desirable to provide a process of making grid lines for a color filter array element obtained by thermal processing which avoids these problems. It would also be desirable to obtain a thermally-transferred color filter array element using the improved process of making grid lines.

These and other objects are achieved in accordance with this invention which comprises a process of making opaque grid lines for a color filter array element comprising:

a) exposing a photographic element comprising an unhardened gelatin-silver halide emulsion coated on a support to light through a mask which defines the grid pattern, said emulsion being coated at a total dry weight coverage of at least 0.5 g/m²);

b) developing the element with a tanning developer to develop the exposed areas of grid lines;

c) washing off the undeveloped emulsion leaving the grid line pattern on the element; and

d) drying the element to produce open cells on the support divided by opaque lines of silver in hardened gelatin greater than 0.3 μm in height above the support.

In a preferred embodiment of the invention, the opaque lines are about 10 μm to 60 μm in width and are separated from each other by 100 to 600 μm, the center-line distance from one mosaic element to another. In another preferred embodiment, the process includes the further steps of:

e) coating the cellular element with a polymeric dye-receiving layer; and

f) thermally transferring individual dyes to form a color filter array element comprising a repeating mosaic pattern of colorants in a polymeric binder, the pattern being made up of color patches bounded by the opaque lines in a grid pattern.

The gelatin-silver halide emulsion used in the invention is a conventional emulsion employed in photography provided it is unhardened. See, for example, "The Theory of The Photographic Process", 3rd edition, Mees and James, 1966, MacMillan Company, pages 304-305. The emulsion may be coated at coverages ranging from 0.4 g/m² to 20 g/m² total dry weight, preferably from 1 g/m² to 10 g/m².

The tanning developers used in the invention are also well known to those skilled in the art as disclosed in the Mees and James reference discussed above. Examples of such developers include in their formulation pyrogallol, catechol, hydroquinone, Metol®, etc. as tanning developing agents.

The mosaic pattern in a color filter array element obtained using the process of the invention in a preferred embodiment consists of a set of red, green and blue additive primaries.

The size of the mosaic set in the thermally-transferred color filter array elements obtained by the process of the invention is not normally critical since it depends on the viewing distance. In general, the individual pixels (mosaic elements) of the set are from about 50 to about 600 μm. They do not have to be of the same size.

In a preferred embodiment of the invention, the repeating mosaic pattern of dye to form the color filter array element consists of uniform, square, linear repeating areas, with one color diagonal displacement as follows: ##STR1##

In another preferred embodiment, the above squares are approximately 100 μm on each edge.

As noted above, the color filter array elements of the invention are used in various display devices such as a liquid crystal display device. Such liquid crystal display devices are described, for example, in UK Patents 2,154,355; 2,130,781; 2,162,674 and 2,161,971.

The polymeric binder employed in the dye image-receiving layer of the invention may comprise, for example, a polycarbonate, a polyurethane, a polyester, a polyamide, a polyacrylonitrile, or mixtures or copolymers thereof, preferably those which are cross-linkable, as described in Simons U.S. Ser. No. 408,340, filed Sept. 18, 1989, and entitled "Thermally-Transferred Color Filter Array Element". The polymeric binder may be present in any amount which is effective for the intended purpose. In general, good results have been obtained at a concentration of from about 0.25 to about 5 g/m².

A cross-linked binder which has a T_(g) greater than 150° C. better enables the colour filter array element to be resistant to the rather severe heating and treatment steps which are necessary in forming a liquid crystal display device. Examples of such cross-linkable polymeric binders include polymers which may be cross-linked by reaction with another substance present in or applied to the layer, such as epoxide resins (reacting with, for example, bifunctional amine compounds or resins, butylated urea, melamine or benzo-guanamine resins or phenolic adducts), unsaturated polyesters (reacting with, for example, organic peroxides), phenolic resins (reacting with, for example, aldehydes), alkyd resins (reacting with, for example, butylated urea, melamine or benzo-guanamine resins) or polyurethanes (reacting with, for example, di-isocyanates); and polymer systems which may be cross-linked on exposure to light, in the presence of photoinitiators or photosensitizers. Several examples of the latter class are described in "Photopolymerization of Surface Coatings" by C. G. Roffey, published by John Wiley and Sons, Chichester, England, 1982, and include as polymers, unsaturated polyesters and polyamides, polyvinyl acetals, polymers with cinnamoyl groups, epoxy resins and polyurethanes, and as photosensitizers, aromatic carbonyl compounds such as benzoin, acetophenones, benzophenones and quinones, and also aryl diazonium compounds and metal carbonyls. A valuable class of photocrosslinkable polymeric materials is described by Purbrick and Wagner in British Patent 2,106,522B, and comprises a polymer bearing nucleophilic groups, such as epoxy, carbonyl, hydroxy, tertiary amino, morpholino, unsaturated nitrogen-containing heterocyclic, or mercapto groups, and radiation-sensitive metal carbonyl compounds, such as benzene chromium tricarbonyl.

The transparent support for the color filter array element produced by the process of the invention may be any transparent material such as polycarbonate, polyethylene terephthalate, cellulose acetate, polystyrene, etc. In a preferred embodiment the support is glass.

A dye-donor element that is used to form the color filter array element of the invention comprises a support having thereon a dye layer. Any dye or mixture of dyes can be used in such a layer provided they are transferable to the dye image-receiving layer of the color array element of the invention by the action of heat. Especially good results have been obtained with sublimable dyes. Examples of sublimable dyes include anthraquinone dyes, e.g., Sumikalon Violet RS® (product of Sumitomo Chemical Co., Ltd.), Dianix Fast Violet 3R-FS® (product of Mitsubishi Chemical Industries, Ltd.), and Kayalon Polyol Brilliant Blue N-BGM® and KST Black 146® (products of Nippon Kayaku Co., Ltd.); azo dyes such as Kayalon Polyol Brilliant Blue BM®, Kayalon Polyol Dark Blue 2BM®, and KST Black KR® (products of Nippon Kayaku Co., Ltd.), Sumickaron Diazo Black 5G® (product of Sumitomo Chemical Co., Ltd.), and Miktazol Black 5GH® (product of Mitsui Toatsu Chemicals, Inc.); direct dyes such as Direct Dark Green B® (product of Mitsubishi Chemical Industries, Ltd.) and Direct Brown M® and Direct Fast Black D® (products of Nippon Kayaku Co. Ltd.); acid dyes such as Kayanol Milling Cyanine 5R® (product of Nippon Kayaku Co. Ltd.); basic dyes such as Sumicacryl Blue 6G® (product of Sumitomo Chemical Co., Ltd.), and Aizen Malachite Green® (product of Hodogaya Chemical Co., Ltd.); ##STR2## or any of the dyes disclosed in U.S. Pat. No. 4,541,830. The above subtractive dyes may be employed in various combinations to obtain the desired red, blue and green additive primary colors. The dyes may be mixed within the dye layer or transferred sequentially if coated in separate dye layers. The dyes may be used at a coverage of from about 0.05 to about 1 g/m².

The dye in the dye-donor element is preferably dispersed in a polymeric binder such as a cellulose derivative, e.g., cellulose acetate hydrogen phthalate, cellulose acetate, cellulose acetate propionate, cellulose acetate butyrate, cellulose triacetate; a polycarbonate; poly(styrene-co-acrylonitrile), a poly(sulfone) or a poly(phenylene oxide). The binder may be used at a coverage of from about 0.1 to about 5 g/m².

The dye layer of the dye-donor element may be coated on the support or printed thereon by a printing technique such as a gravure process.

Any material can be used as the support for the dye-donor element provided it is dimensionally stable and can withstand the heat of the thermal printing process. Such materials include polyesters such as poly(ethylene terephthalate); polyamides; polycarbonates; glassine paper; condenser paper; cellulose esters; fluorine polymers; polyethers; polyacetals; polyolefins; and polyimides. The support generally has a thickness of from about 2 to about 30 μm. It may also be coated with a subbing layer, if desired.

The dye-donor element of the invention may be used in sheet form or in a continuous roll or ribbon.

Various methods may be used to transfer dye from the dye donor to the transparent support to form the color filter array element of the invention. There may be used, for example, a high intensity light flash technique with a dye-donor containing an energy absorptive material such as carbon black or a non-subliming light-absorbing dye. Such a donor is used in conjunction with a mirror which has a mosaic pattern formed by etching with a photoresist material. This method is described more fully in U.S. application Ser. No. 408,581 by Simons filed Sept. 18, 1989.

Another method of transferring dye from the dye donor to the transparent support to form the color filter array element of the invention is to use a heated embossed roller is described more fully in U.S. application Ser. No. 408,580 by Simons filed Sept. 18, 1989.

After the dyes are transferred to the receiver, the image may be treated to further diffuse the dye into the dye-receiving layer in order stabilize the image. This may be done by radiant heating, solvent vapor, or by contact with heated rollers. The fusing step aids in preventing fading upon exposure to light and surface abrasion of the image and also tends to prevent crystallization of the dyes. Solvent vapor fusing may also be used instead of thermal fusing.

The following example is provided to illustrate the invention.

EXAMPLE

A glass plate was coated with a low speed, blue-sensitive silver bromoiodide photographic emulsion to give an approximate coverage of 4 g/m² silver and 2.5 g/m² of gelatin, providing a thickness of about 3 μm. No hardener was used.

The plate was light-exposed through a photographic negative having a two-dimensional pattern of transparent grid lines defining a pattern of opaque squares, the lines being 50 μm wide and forming a square grid of 300 μm edge length. The plate was then given a tanning development process. The plate was:

a) soaked for 10 seconds in 10 g/l sodium sulphite solution in water at room temperature;

b) developed for 20 seconds at 21° C. under nitrogen in the following tanning developer:

    ______________________________________                                         Pyrogallol             2      g/l                                              Metol                  0.67   g/l                                              Sodium sulphite        2.67   g/l                                              Sodium sulphate        100    g/l                                              Sodium carbonate       33     g/l                                              Potassium bromide      2.67   g/l                                              ______________________________________                                    

c) rinsed for 10 second in the solution in a);

d) washed in a gently agitated solution of sodium sulphate, 10 g/l, at 40° C., until the emulsion in the unexposed areas had washed off, leaving the image of the grid on the plate;

e) washed in the solution in b); and

f) dried.

The plate was examined under a microscope and showed a fine, hardened, opaque gelatin grid of approximately 300 μm edge and raised in relief above the surface of the plate, forming an array element of transparent shallow square cells on the surface of the plate.

A 5% solution of vinyl chloride/vinyl acetate copolymer in butanone was run over the surface of the plate and the surplus drained off, so as to form, after drying, a layer of the polymer in each of the cells forming a dye image-receiving layer.

A yellow dye-donor sheet was prepared by coating on a 6 μm poly(ethylene terephthalate) support the following composition from butanone solvent. The carbon was ball-milled in butanone prior to use.

    ______________________________________                                         Yellow Composition                                                             Yellow dye illustrated below                                                                            0.25 g/m.sup.2                                        Cabot Corp.) (Regal 300 ®                                                                           0.76 g/m.sup.2                                        Cellulose acetate propionate                                                                            0.38 g/m.sup.2                                        Yellow Dye-2                                                                    ##STR3##                                                                      ______________________________________                                    

A patterned mirror was then prepared in order to provide a means to transfer dye from the dye-donor in a repeating mosaic pattern to cells of the glass plate described above.

A patterned glass mirror was made by removing the lacquer from the back of a commercially-available glass silvered mirror by treating it with a mixture of dimethyl formamide and cyclohexanone (3:1) at 95° C. for 15 minutes. The revealed metal surface was then coated with a quantity of Kodak Micro Resist 747® photoresist and the excess poured off so as to leave a thin film. It was then dried, exposed through a mask of the desired pattern, developed for about two minutes in Kodak Micro Resist® developer, rinsed for 15 seconds in Kodak Micro Resist® rinse, and then etched in a solution of 400 g/l of FeCl₃.6H₂ O to remove areas of the mirrored surface to give an array of transparent squares of 300 μm edge length. Each square touched the corner of the next square along one diagonal of the array, and was laterally separated from the adjacent clear squares along the orthogonal axes of the array by 600 μm.

The above-prepared yellow dye-donor sheet was placed on the grid on the glass plate, coated side down facing the grid. The patterned mirror was placed, metallized side down, on top of the donor sheet. The assembly was placed on a horizontal illuminated screen, and with the help of a 10× magnifying lens, the mirror was positioned so that its transparent windows (300 μm square) coincided with squares of the grid. The components were clamped in position, and the assembly was exposed to a flash as described below. In the transparent patterned-square areas of the mirror, the high-intensity light passed through to the dye-donor. The carbon in the dye-donor then converted the high-intensity light energy to thermal energy to selectively transfer the dye.

The 7.5×4.5 cm window of a Mecablitz® Model 45 (Metz AG Company) was fitted with a mirror box 6 cm long to reduce the exit aperture to 4.5 cm×4.5 cm. The flash unit was placed with the window of the mirror box against the patterned glass mirror and the flash fired at full intensity. Upon separating the assembly, squares of yellow dye were seen to have transferred into one third of the squares of the opaque, black grid.

The above process was repeated using magenta and cyan donor sheets similar to the yellow donor sheet described above, but using the magenta and cyan compositions described below, the mirror and grid patterns being aligned to place the yellow, magenta and cyan dyes in adjacent squares. The plate was then heated overall to diffuse the dyes into the polymer layer, and then it was flow-coated with a 4% aqueous gelatin solution, the surplus poured off, and the plate dried.

    ______________________________________                                         Magenta Composition                                                            Magenta dye illustrated above                                                                            0.20 g/m.sup.2                                       Cabot Corp.) (Regal 300 ®                                                                            0.58 g/m.sup.2                                       Cellulose acetate propionate                                                                             0.30 g/m.sup.2                                       Cyan Composition                                                               Cyan dye illustrated above                                                                               0.39 g/m.sup.2                                       Cabot Corp.) (Regal 300 ®                                                                            1.17 g/m.sup.2                                       Cellulose acetate propionate                                                                             0.58 g/m.sup.2                                       ______________________________________                                    

A similar filter array element was prepared on a glass plate coated with vinyl chloride/vinyl acetate copolymer, without the grid and not being coated with gelatin, as a control.

The susceptibility of the two array elements to thermal dye migration was tested by holding them at 170° C. for 30 minutes. Microscopic examination showed the array element on the control plate without the grid to have suffered severe diffusion, with the dye patterns badly degraded. On the other hand, the array element deposited on the plate with the grid remained intact, each square of the dye remaining within its 300 μm square grid and the color mosaic being regular and well defined.

This invention has been described in detail with particular reference to preferred embodiments thereof, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention. 

What is claimed is:
 1. A process of making a color filter array element comprisinga) exposing a photographic element comprising an unhardened gelatin-silver halide emulsion coated on a support to light through a mask which defines the grid pattern, said emulsion being coated at a total dry weight coverage of at least 0.5 g/m² ; b) developing said element with a tanning developer to develop the exposed areas of grid lines; c) washing off the undeveloped emulsion leaving the grid line pattern on said element; d) drying said element to produce open cells on said support divided by opaque lines of silver in hardened gelatin greater than 0.3 μm in height above said support; e) coating said cellular element with a polymeric dye-receiving layer; and f) thermally transferring individual dyes to form a color filter array element comprising a repeating mosaic pattern of colorants in a polymeric binder, said pattern being made up of color patches bounded by said opaque lines in a grid pattern.
 2. The process of claim 1 wherein said opaque lines are about 10 μm to 60 μm in width and are separated from each other by 100 μm to 600 μm.
 3. The process of claim 1 wherein said polymeric binder is cross-linked after transfer of said color filter array image.
 4. The process of claim 1 wherein said pattern consists of a set of red, green and blue additive primaries.
 5. The process of claim 1 wherein said support is glass.
 6. The process of claim 1 wherein said binder also contains a cross-linking agent. 